WIRONIUM
WIRONIUM® Cobalt-chrome partial denture alloy
- Top-quality alloy, proven worldwide since 1972 – ideally suited for conventional clasp partial dentures.
- Excellent flow properties – simple processing.
- Particularly suitable for laser welding with Wiroweld welding wire thanks to the reduced carbon content.
- Biocompatible and corrosion-resistant.
- Type 5: Indicated for prosthetic restorations where parts thereof require a combination of high rigidity and strength, e.g. thin removable partial dentures, sections with thin cross-sections, clasps.
| Product details |
|---|
| Composition in % by mass |
| Co 63.0 · Cr 29.5 · Mo 5.0 · Si 1.0 · C · Mn · N |
| Alloy characteristics | Standard values |
| Type (ISO 22674) | 5 |
| Density | 8,2 g/cm3 |
| Preheating temperature | 950–1 050 °C |
| Solidus, liquidus temperature | 1360, 1405 °C |
| Casting temperature approx. | 1 440 °C |
| Young’s modulus | 230 GPa |
| Proof strength (Rp0,2) | 680 MPa |
| Ultimate strength (Rm) | 855 MPa |
| Elongation after fracture (A5) | 15 % |
| Vickers hardness | 345 HV10 |
| Availability | REF |
| WIRONIUM®, 1 kg | 50065 |
| Accessories | REF |
| Wiroweld, Co-Cr laser wire, carbon-free, Ø 0,35 mm | 50003 |
| Wiroweld, Co-Cr laser wire, carbon-free, Ø 0,5 mm | 50005 |
| Cobalt-chrome solder | 52520 |
Related Downloads
-
Bio-certificate
PDF55.8 KB Download File -
Partial denture technique guidelines
PDF5.4 MB Download File -
Safety Data Sheet
PDF236.2 KB Download File -
Instructions for use
PDF82.4 KB Download File